DOW RTV-3483 Silicone (20+1)

₹53999

(Including all taxes)


Product Specification


  • Diamension : .
  • Weight : 21 kg

DOW SILASTIC RTV-3483 Rubber is a two-part material consisting of SILASTIC RTV-3483 Base, which when mixed with SILASTIC RTV-3083 Curing Agent, cures at room temperature by a condensation reaction. A range of materials can be cast into the cured silicone mold: plaster, polyurethane and polyester resins are materials typically used.


TECHNICALS

View Technical Data Sheet


Property

Unit

Result

Base and curing agent mixture (100:5 by weight)

 

 

Mixed viscosity

mPa.s

16,000

Color

 

White

Working time of catalyzed mixture at 23C (73.4F), min

minutes

90-120

Curing time, maximum

hours

24

Cured for 2 days at 23C (73.4F)

 

 

Hardness (Shore A)

 

13

Tensile strength

MPa

3.9

Elongation at break

%

680

Tear strength

kN/m

25

Relative density at 25C (77F)

 

1.16

Linear shrinkage

%

0.2-0.4